Transistor gates including cobalt silicide, semiconductor device structures including the transistor gates, precursor structures, and methods of fabrication

ABSTRACT

A method for fabricating a transistor gate with a conductive element that includes cobalt silicide includes use of a sacrificial material as a place-holder between sidewall spacers of the transistor gate until after high temperature processes, such as the fabrication of raised source and drain regions, have been completed. In addition, semiconductor devices (e.g., DRAM devices and NAND flash memory devices) with transistor gates that include cobalt silicide in their conductive elements are also disclosed, as are transistors with raised source and drain regions and cobalt silicide in the transistor gates thereof. Intermediate semiconductor device structures that include transistor gates with sacrificial material or a gap between upper portions of sidewall spacers are also disclosed.

FIELD OF THE INVENTION

The present invention, in various embodiments, relates generally to methods for fabricating gates of transistors and, more specifically, to methods for fabricating gates that include conductive elements that comprise cobalt silicide, and associated structures. In particular, embodiments of the present invention relate to methods and associated structures in which high temperature processes, such as the fabrication of raised source and drain regions of a transistor, are completed before cobalt silicide features are fabricated.

BACKGROUND OF THE INVENTION

Transistor gates are used in a variety of different types of semiconductor devices. A number of different types of conductive materials have been used to form the elements, or lines, of transistor gates. Tungsten silicide is an example of such a conductive material, and is widely used in semiconductor devices that employ current state-of-the-art technologies.

As feature dimensions of semiconductor device structures decrease, limitations on the materials that are used therein become ever more apparent. For example, at line widths of about 55 nm and less, the bulk electrical resistance of tungsten silicide (WSi_(x)) increases to about 175μΩ to about 250μΩ. Bulk electrical resistances of this magnitude are undesirable, as they decrease the rate at which conductive lines transmit electrical signals and may cause the conductive lines and other elements of a semiconductor device to be heated to temperatures that may adversely affect the performance, structural integrity, and reliability of the semiconductor device.

Cobalt disilicide (CoSi₂) has a much lower bulk resistance than tungsten silicide (e.g., about one tenth or less of the bulk resistance of tungsten silicide), but does not retain its quality when exposed to high temperatures, as are encountered during many semiconductor device fabrication processes. For example, the epitaxial processes that are required to form “raised” (i.e., at the same elevation or a higher elevation than a gate oxide) source and drain regions adjacent to transistor gates of some types of transistors, such as those of dynamic random access memory (DRAM) devices and NAND flash memory devices, require temperatures of 900° C. or more. As a consequence of the relatively low thermal stability of cobalt disilicide, it could not be used in transistors with raised source and drain regions or other structures in which conductive elements have conventionally been fabricated before all high temperature processes have been completed.

Accordingly, there is a need for processes that facilitate the use of lower bulk resistance conductive materials in the fabrication of conductive features of semiconductor devices with ever-decreasing feature dimensions, as well as for semiconductor device structures with conductive features that are formed with low bulk resistance materials.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings, which depict various features of different aspects of the present invention:

FIGS. 1 through 24 depict an embodiment of a process for fabricating a transistor of a semiconductor device structure, in which a gate of the transistor includes a conductive element formed at least partially from cobalt silicide, in which FIG. 1 illustrates a section of a semiconductor device structure under fabrication, FIGS. 2 through 5 show an enlarged, smaller section of a semiconductor device structure under fabrication, and FIGS. 6 through 24 depict an even more enlarged, smaller section of a semiconductor device structure under fabrication;

FIG. 25 illustrates an embodiment of a semiconductor device structure that includes a transistor with a gate including a conductive element that is partially formed from cobalt silicide; and

FIG. 26 is a schematic representation of an embodiment of an electronic device that includes a semiconductor device with one or more transistors that include transistor gates that include conductive elements with cobalt silicide.

DETAILED DESCRIPTION

In one embodiment, the present invention includes methods for fabricating transistor gates, or “word lines,” for semiconductor devices. Such a method includes the use of a sacrificial material as a place-holder until high temperature processes have been completed. As a specific but non-limiting example, the sacrificial material may act as a place-holder between sidewall spacers of a transistor gate until after high temperature epitaxial deposition processes are used to form raised source and drain regions adjacent to opposite sides of the transistor gate. Once high temperature processes have been performed, the sacrificial material may be removed and replaced with cobalt silicide.

According to another embodiment, the present invention includes structures that include cobalt silicide conductive features. One nonlimiting example of such a structure is a transistor of a semiconductor device, such as a DRAM device, a NAND flash memory device, as well as any other transistor that includes raised source and drain regions, and semiconductor devices including such structures.

Embodiments of intermediate semiconductor device structures that include transistor gate structures with sacrificial material or a gap between upper portions of sidewall spacers thereof are also within the scope of the present invention.

Other features and advantages of the present invention will become apparent to those in the art through consideration of the ensuing description, the accompanying drawings, and the appended claims.

One embodiment of a method for fabricating a transistor gate with a conductive element that includes cobalt silicide is shown in FIGS. 1 through 24.

In FIG. 1, a semiconductor device structure 10, including a semiconductor substrate 12 with an active surface 14 and isolation structures 16 (e.g., shallow trench isolation (STI) structures, etc.) formed or fabricated (by any suitable manner known in the art) on or in active surface 14 is depicted.

A gate oxide 18 is formed over active surface 14 by known processes, as shown in FIG. 2. As shown in FIG. 3, a polysilicon layer 20 is then deposited over gate oxide 18 and active surface 14 by any known process (e.g., chemical vapor deposition (CVD), etc.).

Thereafter, as illustrated in FIG. 4, a layer 30 of tantalum silicide (TaSi₂) is formed on or over polysilicon layer 20. Tantalum silicide layer 30 may be formed by any suitable process known in the art, including, but not limited to, a physical vapor deposition (PVD) process (e.g., sputtering). Without limiting the scope of the present invention, tantalum silicide layer 30 may be formed to a thickness of about 200 Å to about 300 Å.

A silicon layer 40 is then formed on or over tantalum silicide layer 30, as depicted in FIG. 5. Silicon layer 40, which may comprise amorphous silicon, or “α-Si,” may be formed by any appropriate, known process (e.g., PVD). By way of non-limiting example, silicon layer 40 may have a thickness of about 300 Å to about 600 Å.

Once the “stack” 35 of tantalum silicide layer 30 and silicon layer 40 has been formed, nitrogen may be implanted through silicon layer 40 and into tantalum silicide layer 30, as illustrated in FIG. 6. Such implantation may be effected by known processes, such as by way of a N₁₄ ⁺ implantation process is effected at a density of 5×10¹⁵ (or 5E15) particles per/cm² at 15 KeV (i.e., a N₁₄ ⁺5E15 15 KeV implantation process is effected).

As FIG. 7 shows, once nitrogen implantation is complete, a thin oxide layer 50 may be formed on an exposed surface 42 of silicon layer 40. As an example, and not to limit the scope of the present invention, thin oxide layer 50 may have a thickness of about 30 Å. Any known process (e.g., high temperature oxidation (HTO), in-situ steam-generated (ISSG) oxide, etc.) may be used to form (e.g., grow, deposit, etc.) thin oxide layer 50 onto exposed surface 42 of silicon layer 40.

As depicted in FIG. 8, a “sacrificial layer 60” may be formed on or over oxide layer 50. Sacrificial layer 60 may comprise n-doped polysilicon, silicon nitride, or any other suitable material, and may be formed by suitable, known processes (e.g., CVD, etc.). Sacrificial layer 60 may have a thickness of about 1,000 Å.

Individual gate stacks 65 may then be formed, as shown in FIGS. 9 and 10. In forming individual gate stacks 65, portions of sacrificial layer 60, oxide layer 50, silicon layer 40, silicide layer 30, and polysilicon layer 20 are removed by known processes. As an example, a mask 70 (e.g., a carbon-based (e.g., transparent carbon) mask, a hard mask, a photomask, etc.) may be formed on or over sacrificial layer 60 by known processes (see FIG. 9), then serve as a pattern through which material removal is effected. The materials of layers 60, 50, 40, 30, and 20 may be removed, for example, by use of one or more suitable etchants (e.g., dry etchants) under process conditions that provide the desired results (e.g., aspect ratios, sidewall shape and orientation, etc.). Material of layer 60 may be removed through apertures 72 in mask 70, while material of each underlying layer 50, 40, 30, 20 may be removed through apertures 72 of mask 70 and/or through openings that are formed in one or more overlying layers 60, 50, 40, 30 as material is removed from the overlying layers.

With reference to FIGS. 11 and 12, sidewall spacers 85 are formed on the lateral edges 67 of each gate stack 65 by known processes. For example, a layer 80 of a suitable dielectric material, i.e., a material that may be removed selectively with respect to the material of remaining portions 60 r of sacrificial layer 60 (FIGS. 8 and 9) (e.g., silicon nitride, silicon oxide, etc., in the case of a polysilicon sacrificial layer 60, a silicon oxide spacer formed by decomposition of tetraethylorthosilicate (TEOS) in the case of a silicon nitride sacrificial layer 60, etc.), may be formed (e.g., blanket deposited) over semiconductor device structure 10, as shown in FIG. 11. Thereafter, as shown in FIG. 12, a spacer etch of a suitable, known type may be effected to define sidewall spacers 85 from portions of layer 80 that are laterally adjacent to lateral edges 67 of gate stacks 65.

Next, as depicted in FIG. 13, material of gate oxide layer 18 is removed from regions 18 e (FIG. 12) of layer 18 that are exposed between adjacent sidewall spacers 85 (FIG. 12) to form individual gate oxide 18 o structures. Removal of the material of regions 18 e of gate oxide layer 18 may be effected by known processes, such as by use of an etchant that removes the material of gate oxide layer 18 with selectivity over the materials of remaining portions 60 r of sacrificial layer 60 (FIGS. 8 and 9) and sidewall spacer 85. Upon removing exposed portions of gate oxide layer 18, portions of active surface 14 of substrate 12 that are located laterally between gate stacks 65 are exposed.

Source and drain regions 71 and 73, respectively, may then be formed on or in the newly exposed regions of active surface 14 of substrate 12, between adjacent gate stacks 65, as FIG. 14 illustrates. The formation of source and drain regions 71 and 73 may be effected by known processes, including, without limitation, deposition, masking, and etching processes to remove silicon from undesired locations. Without limiting the scope of the present invention, known epitaxial processes may be used to form source and drain regions 71 and 73 that protrude from, or are raised relative to, active surface 14 of substrate 12.

A dielectric layer 100 may then be formed to fill the spaces between adjacent gate stacks 65, as shown in FIG. 15. Dielectric layer 100, which may comprise a doped silicon dioxide, or glass (e.g., borophosphosilicate glass (BPSG), phosphosilicate glass (PSG), borosilicate glass (BSG), etc.), may be formed by known processes (e.g., CVD, spin-on glass, etc.).

Regions 102 of the resulting dielectric layer 100 that have elevations that exceed the uppermost surfaces 68 of gate stacks 65 (e.g., the top surface 64 of remaining portions 60 r of sacrificial layer 60) may be removed, as depicted in FIG. 16. Removal of the material of regions 102 may be carried out by known processes. An example of such a process is chemical-mechanical polishing (CMP). The CMP process may be configured to remove the material of dielectric layer 100 at a faster rate than an exposed material of gate stacks 65 (e.g., the polysilicon of remaining portions 60 r of sacrificial layer 60 (FIGS. 8 and 9)) is removed, or “with selectivity over” the exposed material of gate stacks 65. For example, a so-called “stop-on-silicon” (SOS) polishing process may be used.

If any silicon from the epitaxial deposition process is present on top surfaces 64 of remaining portions 60 r of sacrificial layer 60, it may be removed by any known, suitable process, such as a wet etch (e.g., that is timed to remove about 300 Å of material).

Once remaining portions 60 r of sacrificial layer 60 (FIGS. 8 and 9) are exposed through dielectric layer 100 and any silicon present on upper surfaces 64 of remaining portions 60 r, remaining portions 60 r of sacrificial layer 60 may be removed, as shown in FIG. 17. Remaining portions 60 r (FIG. 16) may be removed by known processes. By way of non-limiting example, remaining portions 60 r may be removed by use of an etchant (e.g., tetramethylammonium hydroxide (TMAH), a dry process for removing polysilicon, etc.) that removes the material of sacrificial layer 60 (e.g., polysilicon) with selectivity over the materials of dielectric layer 100 and sidewall spacers. Alternatively, the remaining portions 60 r may be removed through a mask (not shown).

The remaining portions 50 r of thin oxide layer 50 (see FIGS. 8 and 9) may also be removed, as shown in FIG. 18. Removal of remaining portions 50 r may be effected by any suitable, known process, and with selectivity over the N-implanted α-Si of remaining portions 40 r of silicon layer 40 (see FIGS. 8 and 9).

Thereafter, as illustrated in FIG. 19, remaining portions 30 r of tantalum silicide layer 30 (see FIGS. 8 and 9) may again be subjected to nitrogen implant processes through the newly exposed remaining portions 40 r of silicon layer 40 (see FIGS. 8 and 9). Without limiting the scope of the present invention, a known N₁₄ ⁺5E15 15 KeV implantation process may be employed. Such implantation may be useful for improving the barrier properties of remaining portions 30 r of tantalum silicide layer 30 (FIGS. 8 and 9).

At this point in the process flow, any native oxide that has been formed on the exposed surfaces 42 of remaining portions 40 r of silicon layer 40 (see FIGS. 8 and 9) may be removed by any suitable preclean process (e.g., use of a wet etchant).

FIG. 20 shows the subsequent, successive deposition of a cobalt layer 90 and a titanium or titanium nitride layer 95. Known processes (e.g., chemical vapor deposition (CVD), atomic layer deposition (ALD), physical vapor deposition (PVD) (e.g., sputtering), etc.) may be used to form cobalt layer 90 and titanium layer 95. When low pressure sputtering (ALPS) processes are used to form cobalt layer 90, cobalt layer 90 may have good step coverage (e.g., about 80% bottom step coverage on the largest critical dimensions (CD) of the transistor gate to about 60% bottom step coverage on the smallest CD of the transistor gate). Titanium or titanium nitride layer 95 prevents oxidation of cobalt layer 90 during subsequent processing.

After cobalt layer 90 and titanium or titanium nitride layer 95 have been formed, suitable, known rapid thermal processing (RTP) techniques, may be used to anneal portions of cobalt layer 90 to adjacent, contacted remaining portions 40 r of silicon layer 40 (see FIGS. 8 and 9), as depicted in FIG. 21. Without limiting the scope of the present invention such RTP, which may also be referred to as a “first RTP” or as a “first anneal,” may be effected at a temperature of about 450° C. to about 550° C. for a duration of about thirty seconds in a nitrogen (N₂) environment. The result of the RTP is cobalt monosilicide (CoSi) 92, which is also referred to herein as “cobalt silicide.”

Once annealing has taken place, titanium layer 95 and unreacted regions 90 u of cobalt layer 90 (see FIG. 21) may be removed, or “stripped,” as shown in FIG. 22. Known removal processes (e.g., etching processes, etc.) may be used. As a nonlimiting example, titanium layer 95 and unreacted regions 90 u of cobalt layer 90 may be removed in a so-called “piranha” environment (e.g., at a temperature of about 90° C. for a duration of about 90 seconds), with hot sulfuric acid (e.g., at a temperature of about 90° C. to about 100° C. for a duration of about 90 seconds), or with any other suitable etchants, strippers, or solvents. The process that is used to remove unreacted regions 90 u may have selectivity for cobalt over cobalt silicide.

After titanium layer 95 and unreacted regions 90 u of cobalt layer 90 (see FIG. 21) have been removed, further RTP may be performed on the cobalt monosilicide 92. Such RTP may also be referred to as a “second RTP” or as a “second anneal.” Without limiting the scope of the present invention, this RTP may include exposing cobalt monosilicide 92 to a temperature of about 750° C. to about 850° C. in a nitrogen (N₂) environment for a duration of about thirty seconds. The result is cobalt disilicide (CoSi₂) or, simply “cobalt silicide.”

As depicted in FIGS. 23 and 24, transistor gate caps 112 may be formed by blanket depositing a layer 110 of a suitable dielectric material (e.g., silicon nitride when sidewall spacers 85 are formed from silicon nitride, any suitable interlayer dielectric (ILD) material, glass (e.g., BPSG), or the like when sidewall spacers 85 comprise silicon dioxide, etc.), then removing (e.g., by CMP, wet etch processes, etc.) regions of layer 110 that are not located between sidewall spacers 85.

Remaining regions of dielectric layer 100, or merely portions thereof, as shown in FIG. 25, may then be removed from between sidewall spacers 85 of adjacent transistor gates 69 to form contact holes 105 that expose source and drain regions 71 and 73. Further processing of semiconductor device structure 10, including, but not limited to, the formation of contact plugs (not shown) (e.g., polysilicon plugs, tungsten plugs, etc.) over source and drain regions 71 and 73, may then be conducted in any suitable manner known in the art to fabricate complete semiconductor devices.

With continued reference to FIG. 25, a transistor gate 69 that results from the processes described herein may include a conductive element with a polysilicon layer 20 r, an about 200 Å to about 300 Å thick tantalum silicide layer 30 r, and an about 300 Å to about 600 Å thick cobalt silicide layer 92. As shown, a contact hole 105 may be formed (e.g., by suitable mask and etch processes) between adjacent transistor gates 69 to expose a source or drain region 71, 73 located laterally between adjacent transistor gates 69.

Turning now to FIG. 26, an electronic device 200 that includes a semiconductor device 202 with a transistor gate with a conductive element that comprises cobalt silicide is shown. The semiconductor device 202 may comprise a memory device, such as a DRAM device or a NAND flash memory device. Examples of electronic devices 200 that include NAND flash memory include, but are not limited to, portable digital music players (e.g., MP3, IPOD®, etc.), universal serial bus (USB) drives, removal storage cards, cellular telephones, cameras, and other electronic devices in which it is desirable to retain memory without power.

Although the foregoing description contains many specifics, these should not be construed as limiting the scope of the present invention, but merely as providing illustrations of some of the presently preferred embodiments. Similarly, other embodiments of the invention may be devised which do not depart from the spirit or scope of the present invention. Features from different embodiments may be employed in combination. The scope of the invention is, therefore, indicated and limited only by the appended claims and their legal equivalents, rather than by the foregoing description. All additions, deletions and modifications to the invention as disclosed herein which fall within the meaning and scope of the claims are to be embraced thereby. 

1. A method for fabricating a transistor gate of a memory device, comprising fabricating at least a portion of a conductive element of the transistor gate from cobalt silicide.
 2. The method of claim 1, wherein the act of fabricating is effected following all processes in which process temperatures of about 900° C. or greater are employed.
 3. The method of claim 1, wherein the act of fabricating includes: removing a sacrificial material from between sidewall spacers of the transistor gate; and replacing the sacrificial material with cobalt silicide.
 4. The method of claim 3, wherein removing comprises exposing silicon between the sidewall spacers.
 5. The method of claim 4, wherein replacing comprises introducing cobalt between the sidewall spacers.
 6. The method of claim 5, wherein replacing further comprises annealing the cobalt and the silicon.
 7. The method of claim 6, wherein annealing includes a first anneal in which cobalt silicide is formed.
 8. The method of claim 7, further comprising providing a cap over the cobalt.
 9. The method of claim 8, wherein providing the cap includes providing a cap comprising titanium or titanium nitride over the cobalt.
 10. The method of claim 8, wherein the first anneal is effected with the cap in place.
 11. The method of claim 10, further comprising removing the cap following the first anneal.
 12. The method of claim 11, further comprising additionally annealing the cobalt and the silicon in a second anneal to form cobalt disilicide.
 13. The method of claim 12, wherein the second anneal is effected after removing the cap.
 14. The method of claim 7, wherein annealing also includes a second anneal in which cobalt disilicide is formed.
 15. The method of claim 1, comprising a method for fabricating a transistor gate of a dynamic random access memory.
 16. The method of claim 1, comprising a method for fabricating a transistor gate of a NAND flash memory device.
 17. A method for fabricating a transistor gate, comprising: providing a gate oxide upon a semiconductor substrate; providing at least one layer comprising conductive material over the gate oxide; providing silicon over the at least one layer comprising conductive material; providing a sacrificial layer over the at least one layer comprising conductive material; removing portions of the sacrificial layer, the silicon, and the at least one layer comprising conductive material to form at least one gate stack; providing sidewall spacers on lateral edges of the at least one gate stack; providing active-device regions adjacent to sidewall spacers on each side of the at least one gate stack; providing a dielectric layer over the active-device regions; removing remaining portions of the sacrificial layer; introducing cobalt silicide between the sidewall spacers; and providing a gate cap over the cobalt silicide.
 18. The method of claim 17, wherein providing at least one layer comprising conductive material comprises providing a layer comprising at least one of polysilicon and tantalum silicide over the gate oxide.
 19. The method of claim 18, wherein providing comprises providing a layer comprising polysilicon over the gate oxide and a layer comprising tantalum silicide over the layer comprising polysilicon.
 20. The method of claim 19, wherein providing comprises providing a layer comprising tantalum silicide with a thickness of about 200 Å to about 300 Å.
 21. The method of claim 19, further comprising implanting the layer comprising tantalum silicide with nitrogen species.
 22. The method of claim 21, wherein implanting is effected through the silicon.
 23. The method of claim 17, wherein providing silicon comprises forming a layer comprising amorphous silicon.
 24. The method of claim 17, wherein providing silicon comprises providing a film that comprises silicon and has a thickness of about 300 Å to about 600 Å.
 25. The method of claim 17, further comprising: implanting remaining portions of the tantalum silicide with nitrogen species.
 26. The method of claim 25, wherein implanting remaining portions of the tantalum silicide is effected through remaining portions of the silicon.
 27. The method of claim 17, wherein providing the sacrificial layer comprises providing a sacrificial layer having a thickness of about 1,000 Å.
 28. The method of claim 17, wherein providing the sacrificial layer comprises providing a layer comprising polysilicon.
 29. The method of claim 28, wherein providing sidewall spacers comprises providing sidewall spacers comprising silicon nitride or silicon dioxide.
 30. The method of claim 17, wherein providing the sacrificial layer comprises providing a layer comprising silicon nitride.
 31. The method of claim 30, wherein providing sidewall spacers comprises providing sidewall spacers comprising silicon dioxide.
 32. The method of claim 31, wherein providing sidewall spacers comprising silicon dioxide comprises decomposing tetraethylorthosilicate to deposit the silicon dioxide on sidewalls of the at least gate stack.
 33. The method of claim 17, wherein providing active-device regions comprises epitaxially depositing silicon.
 34. The method of claim 17, further comprising: planarizing the dielectric layer to expose the remaining portions of the sacrificial layer.
 35. The method of claim 17, further comprising: after removing remaining portions of the sacrificial layer, implanting remaining portions of the tantalum silicide layer with nitrogen species.
 36. The method of claim 17, further comprising: providing a thin oxide layer over the silicon before providing the sacrificial layer.
 37. The method of claim 36, wherein providing the thin oxide layer comprises providing a thin oxide layer having a thickness of about 30 Å.
 38. The method of claim 36, further comprising: removing the thin oxide layer after removing the remaining portions of the sacrificial layer.
 39. The method of claim 17, wherein introducing cobalt silicide between the sidewall spacers includes: providing a film comprising cobalt in contact with the silicon; and annealing the cobalt and the silicon.
 40. The method of claim 39, further comprising: providing a film comprising titanium or titanium nitride over the film comprising cobalt.
 41. The method of claim 40, wherein annealing comprises performing a first anneal with the film comprising titanium or titanium nitride in place, the first anneal forming CoSi.
 42. The method of claim 41, further comprising: removing the film comprising titanium or titanium nitride after the first anneal.
 43. The method of claim 42, further comprising: performing a second anneal after removing the film comprising titanium or titanium nitride, the second anneal forming CoSi₂.
 44. The method of claim 43, wherein performing the second anneal results in a layer comprising CoSi₂ and having a thickness of about 300 Å to about 600 Å.
 45. A semiconductor device including at least one transistor with a transistor gate that comprises a conductive element including cobalt silicide.
 46. The semiconductor device of claim 45, wherein the at least one transistor includes raised source and drain regions.
 47. The semiconductor device of claim 45, wherein the conductive element also includes tantalum silicide beneath the cobalt silicide.
 48. The semiconductor device of claim 47, wherein the tantalum silicide has a thickness of about 200 Å to about 300 Å.
 49. The semiconductor device of claim 47, wherein the cobalt silicide has a thickness of about 300 Å to about 600 Å.
 50. The semiconductor device of claim 47, wherein the conductive element also includes conductively doped polysilicon beneath the tantalum silicide.
 51. The semiconductor device of claim 45, comprising dynamic random access memory.
 52. The semiconductor device of claim 45, comprising a NAND flash memory device.
 53. A transistor, comprising: a transistor gate including: a conductive element comprising cobalt silicide; and sidewall spacers adjacent to lateral edges of the conductive element; and a raised source region located adjacent to a first side of the transistor gate; and a raised drain region located adjacent to a second side of the transistor gate.
 54. The transistor gate of claim 53, wherein the conductive element further comprises tantalum silicide beneath the cobalt silicide.
 55. The transistor gate of claim 54, wherein the conductive element further comprises conductively doped polysilicon beneath the tantalum silicide.
 56. An intermediate transistor structure of a semiconductor device structure, comprising: a partially formed transistor gate, including: a pair of sidewall spacers; a partially formed conductive element between lower portions of the sidewall spacers; and a sacrificial material over the partially formed conductive element and between upper portions of the sidewall spacers.
 57. The intermediate transistor structure of claim 56, further comprising: a gate oxide upon which the partially formed transistor gate resides.
 58. The intermediate transistor structure of claim 57, further comprising: a raised source adjacent to a first side of the transistor gate; and a raised drain adjacent to a second side of the transistor gate.
 59. An intermediate transistor structure of a semiconductor device structure, comprising: a partially formed transistor gate, including: a pair of sidewall spacers; a partially formed conductive element between lower portions of the sidewall spacers; and a gap over the partially formed conductive element and between upper portions of the sidewall spacers.
 60. The intermediate transistor structure of claim 59, further comprising: a gate oxide upon which the partially formed transistor gate resides.
 61. The intermediate transistor structure of claim 60, further comprising: a raised source adjacent to a first side of the transistor gate; and a raised drain adjacent to a second side of the transistor gate.
 62. An electronic device, comprising at least one semiconductor device including at least one transistor with a transistor gate comprising a conductive element including cobalt silicide. 